Titanium Corrosion In Molten Glasses Part 2: Electrochemical Study And Corrosion Mechanisms

In situ electrochemical experiments are carried out to determine the mechanisms of pure titanium corrosion in molten glasses. The corrosion layers formed at the metal/glass interface are systematically reported.

Author
C Rapin Et Al
Origin
University Henri Poincare, France
Journal Title
Glass Sci Technol 77 2 2004 88-94
Sector
Special Glass
Class
S 2769