The glass forming region in the P205-A2Mo04-A20 (A=Li, Na) ternary system has been determined. The glass transition temperature (Tg) was mainly controlled by the packing density of the glass network. For glasses of the binary P205-A2Mo04 systems Tg and oxygen packing density increase and then decrease with increasing A2Mo04 contents.
Origin
Lab Chimie Minerale Appliquee, Morocco
Journal Title
Phys Chem Glasses 40 4 1999 229-234
Sector
Special Glass
Class
S 1745