Surface Stress Effects On Indentation Fracture Sequences

Ion exchange was used to introduce surface compression in soda-lime-silica glass and aluminosilicate glass. In situ observations of the indentation cracking sequences on the modified surfaces were made and compared with those on the base glasses.

Author
R Tandon, D J Green, R F Cook
Origin
Pennsylvania State University, Ibb Research Division
Journal Title
J Am Ceram Soc 1990 73 9 2619-2627
Sector
General
Class
G 482

Request article (free for British Glass members)

Surface Stress Effects On Indentation Fracture Sequences
J Am Ceram Soc 1990 73 9 2619-2627
G 482