Comment On "Direct Observation And Analysis Of Indentation Cracking In Glasses And Ceramics"

In commenting on a recent review paper on indentation cracking, the author points out that he has carried out an extensive amount of high-speed photographic work on dynamic indentation cracking of fused silica and simple ionic crystals, which clearly shows the sequence of formation of median and half-penny cracks during loading.