The nucleation rate (I) versus temperature type of curves for a Na20.2Ca0.3Si02(NC2S3) glass doped with 0.1 wt% platinum, 0.5 wt% Ag20, and 2.0 wt% P205 were determined using a previously developed differential thermal analysis (DTA) technique. In this technique, a constant amount of glass sample was nucleated at selected temperatures for a specific time, followed by a DTA scan at a fixed heating rate.