Water Entry Into Silica Glass During Slow Crack Growth

Hydrogen concentration depth profiles on surfaces of SiO2 glass were determined by nuclear reaction analysis. It was found that water enters SiO2 glass during slow crack growth.

Author
M Tomozawa, W-T Han
Origin
Rensselaer Polytechnic Ins.,State University Of New York
Journal Title
J Am Ceram Soc 1991 74 10 2573 - 2576
Sector
Special Glass
Class
S 601