Titanium Corrosion In Molten Glasses: Part 1 - Immersion Tests And Corrosion Kinetics

The kinetics and mechanisms of pure titanium corrosion in three glass melts are investigated in the 1050 to 1400 deg C temperature range by immersion tests. The corrosion layers formed at the metal/glass interface, the elemental concentration profiles in the glass sand the corrosion rates are determined. Corrosion rates are reported on an Arrhenius diagram for each glass.

Author
R Podor Et Al
Origin
Universite Henri Poincare, France
Journal Title
Glass Sci Technol 77 1 2004 36-43
Sector
Special Glass
Class
S 2695