Subcritical Crack Growrth In Soda-Lime Glass Under Combined Modes I And Iii Loading

Fracture and subcritical crack-growh characteristics under combined Modes I and III loading were studied using the modified compact tension specimens of soda-lime glass.

Author
M Yoda
Origin
Nihon University
Journal Title
J Am Ceram Soc 1990 73 7 2124-2127
Sector
General
Class
G 462

Request article (free for British Glass members)

Subcritical Crack Growrth In Soda-Lime Glass Under Combined Modes I And Iii Loading
J Am Ceram Soc 1990 73 7 2124-2127
G 462