Stress Corrosion Cracking Of A Bioactive Glass Composite

Bioactive glass was reinforced with 20 vol% Ag particles and 20 vol% SiC whiskers. Fatigue parameters and lifetime data were determined via the stressing rate dependence of the bend strength in a bio-simulating buffered solution.