Residual Stress Decay Of Indentation Cracks

The length of radial cracks in Vickers indented soda-lime glass and the maximum optical retardation were measured as a function of time at room temeprature in air. The role of water diffusion in the variation of stress decay rate is discussed.

Author
W T Han, P Hrma, A R Cooper
Origin
Case Western Reserve University
Journal Title
Phys Chem Glasses 1989 30 1 30-33