Physicochemical Properties And Ir Spectra Of Glass Forming Sb2O3 (In Russian) Y P Kutsenko Et Al.

The Sb2O3 glass was synthesized from chemically pure Sb2O3 crystals at 750 degrees C in vacuum. This glass is highly resistant to acid corrosion (e.g. HNO3, H2So4). Its properties include a density of 5.06 g/cm3; microhardness, 430 kg/mm2; initial softening temperature, 230 degrees; initial crystallization temperature, 273 degrees; crystallization capacity coefficient, 6.75; refractive index, 2.20; forbidden-band energy, 3.81 eV; and ultrasonic wave propagation rate, 2.62 x 10 power 5 cm/s. The ir spectrum of the glass is compared with that of the crystalline modifications senarmontite and valentinite.

Author
Y A Kutsenko Et Al.
Origin
Unknown
Journal Title
Fiz. Khim. Stekla 1979 5 4 438-441
Sector
Primary Papers
Class
PP 1537

Request article (free for British Glass members)

Physicochemical Properties And Ir Spectra Of Glass Forming Sb2O3 (In Russian) Y P Kutsenko Et Al.
Fiz. Khim. Stekla 1979 5 4 438-441
PP 1537
Are you a member?
This question is for testing whether or not you are a human visitor and to prevent automated spam submissions.
9 + 5 =
Solve this simple math problem and enter the result. E.g. for 1+3, enter 4.