Physical Properties Of Barrier Ribs Of Plasma Display Panels: 1, Formation Of Pores During Sintering Of Lead Borosilicate Glass Frits

The effects of chemical compositions on the sintering behaviour and physical properties of lead borosilicate glass developed for barrier ribs of plasma display panels were investigated. The formation of pores during sintering of the glass was noted, and their formation mechanism investigated using XPS, TG/DTA, and XRD. A change in the oxidation state of the lead was discussed as a possible cause for the formation of pores in the sintered samples.

Author
G Hwang Et Al
Origin
Hongik University, Seaul
Journal Title
J Am Ceram Soc 85 12 2002 2956-2960
Sector
Special Glass
Class
S 2471

Request article (free for British Glass members)

Physical Properties Of Barrier Ribs Of Plasma Display Panels: 1, Formation Of Pores During Sintering Of Lead Borosilicate Glass Frits
J Am Ceram Soc 85 12 2002 2956-2960
S 2471
Are you a member?
This question is for testing whether or not you are a human visitor and to prevent automated spam submissions.
18 + 1 =
Solve this simple math problem and enter the result. E.g. for 1+3, enter 4.