Influence Of Composition On Fatigue Behaviour And Threshold Stress Intensity Factor Of Borosilicate Glasses

Fatigue behaviour of borosilicate glasses was studied using the analysis of subcritical propagation of Vickers indentation cracks. Glasses containing various amounts of glass-network modifiers, mainly soda, were considered.

Author
M Bertoldi & V M Sglavo
Origin
Universita Di Trento, Italy
Journal Title
J Am Ceram Soc 85 10 2002 2499-2506
Sector
Special Glass
Class
S 2419