Influence Of Additives On Slag Resistance Of Al203-Si02-Sic-C Refractory Bond Phases Under Reducing Atmosphere

The microstructures of Al203-Si02-SiC-C refractory matrices with aluminium, silicon, Si3N4, BN, B203, and B4C additives are characterized before and after a crucible slag test, and the phases present are compared to those expected at thermodynamic equilibrium.