Indentation Behavior Of Ion-Exchanged Glasses

Indentation fracture mechanics has been extended to include the effect of a thin layer of residual stress on the indentation strength of brittle materials. The proposed theory was used to predict the residual stress values for an ion-exchanged glass.

Author
R Tandon, D J Green
Origin
The Pennslyvania State University
Journal Title
J Am Ceram Soc 1990 73 4 970-977