Glass-forming regions, valence states, and viscosities in silica-lead oxide systems containing various transition-metal oxides as a third component were investigated.
Origin
Technological University Of Nagayoka
Journal Title
J Am Ceram Soc 1989 72 1 163-165
Sector
Special Glass
Class
S 228