Failure Of Crossply Ceramic-Matrix Composites

The fast-fracture and stress rupture of a crossply ceramic-matrix composite with a matrix through-crack are examined numerically to assess the importance of fibre architecture and the associated concentration at the 0/90 ply interface on failure.