Effect Of Some Nucleating Agents On Thermal Expansion Behaivour Of Li2O-Ba0-Al203-Sio2 Glasses And Glass-Ceramics

The thermal expansion behaviour of some glasses and glass-ceramics within the system spodumene (LiAlSi2O6) - celsian (BaAl2Si2O8) containing LiF, TiO2 and Cr2O3 as nucleation catalysts was described. LiF and TiO2 were found to increase the thermal expansion of the glasses investigated, whereas Cr2O3 slightly lowered the expansion coefficient. The dilatometric transition and softening points of the glasses showed the reverse behaviour. The thermal expansion of the glass-ceramics was a function of type and amount of nucleating agent and heat treatment which greatly affected the mineralogical constitution of the materials.