Dynamic fatigue experiments have characterised the fracture behaviour of ultralow expansion glass in a humid environment as a function of surface finish.
Origin
Unknown
Journal Title
Adv Ceram Mater 1987 2 3A 219-221
Sector
General
Class
G 66